Sankalp Alloys Overseas is one of the promising Manufacturers and suppliers of various metal works. We have been giving a wide level of things beginning with one side of the planet then onto the following. Our thing is extensive of SS 304/304L/304H Sheets & Plates. These Sheets & Plates have been commended well for its choice welding properties. It is the most versatile and low-temperature limits among various grades. It might be really hardened regardless, when it is treated with cold working. Along these lines, it is well off in chromium parts and that is the supporting of its surprising foe of rusting attributes.
All the Stainless Steel grades 304, 304L, and 304H are wrongly Alloyed with the parts like chromium, phosphorus, silicon, manganese, carbon, sulfur, molybdenum, and nickel. Other than various parts chromium, molybdenum, and nickel are the immense accomplices in the whole alliance. In this way, it shows tremendous yield as well as rigidities, astounding temperature resistance, and prolongation range. When in doubt, every one of the three grades are being conceded through the most unimaginable limitation of 40%. In addition, they have the primary dissolving point at 1400 degrees Celsius (or 2550 degrees Fahrenheit) close to the 304H. Grade 304H has a conditioning reach from 2550 to 2590 degrees Fahrenheit.
SS 304/304L/304H Sheets & Plates are exceptionally utilized by the paper and squash encounters, material stuff Manufacturer, condensers in oil based item and nuclear fuel age stations, and petrochemical managing stuff creators. The speculation behind the subtleties of these grade Sheets & Plates is tended to by the ASTM A240 and ASME SA240 rules.
They are generally applied in the get-together of force exchangers and made method vessels, giant haulers, or cutoff. They are gotten an eliminate from the chance to use for the vehicle lines because of their essential straightforwardness and cost-obliging nature. Grade 304 is basically referred to in the fields of food endlessly overseeing endeavors as they are hostile to upsetting as well as high-temperature connectors. These Sheets & Plates are being used contrastingly in the Alloyional and constructional business for its high strain and stress absorbance attributes.
SS 304/304L/304H Sheets & Plates additionally goes through collection testing like PMI tests, IGC test, planned evaluation, mechanical tests, evening out test, radiating test, huge augmentation/more unassuming than standard tests, fumigation test, positive material examination, etc.
304/304L/304H Stainless Steel Sheets & Plates Equivalent Grades
|SS 304||S30400||1.4301||Z7CN18‐09||X5CrNi18-10||SUS 304||304S31||08Х18Н10|
|SS 304L||S30403||1.4306/1.4307||Z3CN18‐10||X2CrNi18-9 / X2CrNi19-11||SUS 304L||304S11||03Х18Н11|
Specification of Stainless Steel 304/304L/304H Sheets & Plates
Stainless Steel Sheets & Plates Specification : ASTM A240 / ASME SA240
Dimension Standard : JIS, AISI, ASTM, GB, DIN, EN, etc
Width : 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc
Length : 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc
Thickness : 0.3 mm to 120 mm
Form : Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange) etc.
Surface Finishing : Hot rolled plate (HR), Cold rolled sheet (CR),2B, 2D, BA, NO.1, NO.4, NO.8, 8K, mirror, Chequered, embossed, hair line, sand blast, Brush, etching, SATIN (Met with Plastic Coated) etc.
Chemical Alloyion of Stainless Steel 304/304L/304H Sheets & Plates
|304||0.07max||2.0max||0.75max||0.045max||0.03max||min: 18.0 max: 20.0||min: 8.0 max: 10.5||—|
|304L||0.03max||2.0max||0.75max||0.045max||0.03max||min: 18.0 max: 20.0||min: 8.0 max: 12.0||0.10 max|
Mechanical Properties Of Stainless Steel 304/304L/304H Sheets & Plates
|Grade||Tensile Strength ksi (min)||Yield Strength 0.2% ksi (min)||Elongation %||Hardness (Brinell) MAX||Hardness (Rockwell B) MAX|
Physical Properties of 304/304L/304H Stainless Steel Round Bar
(BTU/h ft. °F)
(in x 10-6)
(psi x 106
°F x 10-6
|at 68°F: 0.285||9.4 at 212°F||28.3 at 68°F||28||9.4 at 32 – 212°F||0.1200 at 68°F to 212°F||2500 to 2590|
|12.4 at 932 °F||39.4 at 752°F||10.2 at 32 – 1000°F|
|49.6 at 1652 °F||10.4 at 32 – 1500°F|
Thermal Expansion (min/in)-°F
|Thermal Conductivity BTU/hr-ft-°F||Specific Heat BTU/lbm -°F||Modules of Elasticity (annealed)2-psi|
|at 68 °F||at 68 – 212°F||at 68 – 1600°F||at 212°F||at 932°F||at 32 – 212°F||in tension (E)|
|0.285||9.2||11.0||9.4||12.4||0.12||29 x 106|